Per calor curatio Aluminium et Aluminium Alloys, variis exitibus sunt communiter offendit, ut:
-Improper pars collocatione: hoc potest ad partem deformationis, saepe debitum ad insufficiens calor remotionem per extinxit medium ad ieiunium satis ad consequi desideravit mechanica proprietatibus.
-Rapid calefactio: hoc potest consequuntur in scelerisque deformatio; Preme part collocatione adjuvat curare etiam calefactio.
-Overheating: Hoc potest ad partialem liquescens vel eutectic liquescens.
-Surface scaling / summus temperatus oxidation.
-Excessive aut insufficiens canus curatio, utrumque potest consequuntur in damnum mechanica proprietatibus.
-Flectuations in tempore / caliditas / extinguendas parametri potest causare deviationes in mechanica et / vel physica inter partes et batches.
-Additionally, pauperem temperatus uniformitatem, insufficiens velit tempus, et insufficiens refrigerationem in solution calor curatio potest omnes contribuere ad insufficiens results.
Calor curatio est crucial scelerisque processus in aluminium industria, lets 'in magis related scientia.
1.Pre, curatio
Pre-treatment processus quod amplio structuram et sublevare accentus ante extinxit sunt utilis reducing distortione. Pre-treatment typically involves processibus sicut sphaerens annexa et accentus relevium annealing, et quidam etiam adopt extinguendo et temperatio vel normalizing curatio.
Suspendisse subsidio annealing: Per machining, RELICTUM passiones potest develop debitum ad factores sicut machining modi, tool proelio et cutting. Inaequaliter distribution horum passiones potest ad distortionem per extinxit. Ut mitigare hos effectus, accentus relevium annealing ante extinxit necesse est. Et temperatus pro accentus relevium annealing est fere 500-700 ° c. Cum calefactio in aere medium, a temperatus de 500-550 ° C et tenens tempus 2-3 horas adhibetur ne oxidatio et decarburization. Ex parte distortionem debitum ad sui-pondus debet considerari durante loading, et alia procedendi sunt similis vexillum annales.
Preheat curatio ad structuram lenimentus: Hoc includit sphaeram Annealing, extinguens et temperatio, normalizing curatio.
-Pheroidizing annales: Essential ad ipsum Steel et mixturae instrumentum ferro in calor curatio, in structuram adeptus post explendis Annealing significantly afficit ad distortionem trend per extinxit. Per adjusting post-annealing structuram, potest reducere iusto distortione per extinxit.
-Other pre-curatio modi: Variis modi potest esse usus ad redigendum extinguetur distortione, ut extinguantur et temperatio, normalizing curatio. Delectos idoneam pre-treatments sicut extinxit et temperatio, normalizing curatio fundatur super causam distortionem et materiam ex parte potest efficaciter reducere distortione. Sed cautio est necessarium RELICTUM passiones et duritiem crescit post temperiam, praesertim extinxit et temperatio curatio potest reducere expansionem in extinguendo in reducing deformatio ad Steels ut GCER55.
In practical productio, identifying causam extinxit distortione, utrum suus 'debitum ad residualem passes et pauper structuram, est essentialis ad effective curatio. Accentus relevium annealing debet conducted ad perturbationem fecit a RELICTUM passiones, cum treatments sicut temperatio quod mutare structuram non necessaria, et e converso. Tantum tunc potest finis reducendo extinguetur distortionem esse effectum ad minus sumptibus et ensure qualitas.
2.quenching calefactio operatio
Temperature extinguitur: Quod extinguitur temperatus significantly afficit distaturam. Possumus consequi ad reducendo deformatio a adjusting in extinxit temperatus, vel reservatur machining grande est idem quod extinxit temperatus ad consequi ad reducendo deforment et restitue temperatus ad calor curatio, seu extinguitur temperatus post calor curatio probat , Ut ad redigendum subsequent machining cibaria. Quod effectus extinxit temperatus in extinguere deformatio non solum ad materiam usus est in workpiece, sed etiam ad magnitudinem et figura de workpiece. Cum autem figura et magnitudine workpiece sunt diversa, quamvis materia workpiece est idem, quod extinguat deformatio flecte satis differt, et operator operam ad hoc situ in ipsa productio.
Quenching tenens Tempus: Quod lectio tenens tempus non solum ensures penitus calefactio et perveniendi desideravit duritiam vel mechanica proprietates post extinxit sed etiam considerat effectum in distortione. Extendens extendens tenens tempus per se crescit extinguendo temperatus, praesertim pronuntiata summus ipsum et summus chromium ferro.
Loading modi: Si in workpiece ponitur in ratione formam durante calefactio, quod erit causa deformatio debitum ad pondus workpiece vel deformatio debitum ad mutua extrusionem inter workpieces, aut deformatio ex inaequaliter et refrigerationem debitum ad nimia et inaequalis.
Calefactio modum: Nam complexu-informibus et varia crassitudine workpieces, praesertim illi cum altum ipsum et mixturae elementa, tardus et uniformis calefactio processus est crucial. Utiendis preheating est saepe necessarium, nunc postulantes multa prheheating circuitus. Nam maior workpieces non efficaciter tractata per preheating, usura buxum resistentia fornacem cum regiendis calefacit potest reducere perturbatione fecit per celeri calefactio.
III. Refrigeranda operatio
Extinguitur deformatio praesertim ex refrigerationem processus. Propriis extinguere medium lectio, sapiens operatio, et quisque gradum ad refrigerationem processum directe influere extinguetur deformatio.
Selectio extinguatur medium: Dum ensuring desideravit duritiam post-extinxit, mitior extinxit media debet malle ut minimize distortione. Per calefacit balneum mediis ad refrigerationem (ut faciliorem erigens dum pars adhuc calidum) vel etiam aer refrigerationem commendatur. Medium cum refrigerationem rates inter aqua et oleum potest etiam reponere aquam, oleum dual mediis.
-Aair-refrigerationem extinguantur: Aeris-refrigerationem extinxit est efficax ad reducing in extensionem deformatio summus celeritate ferro, Chromium Fingunt ferro et aere-refrigerationem Micro-deformatio ferro. Nam 3r2w8v ferro quod non requirere princeps duritia post extinguantur, aer extinguere potest etiam ad redigendum deformatio per proprie adjusting extinguendo temperatus.
-Oil refrigerationem et extinguantur: oil is a quenching medium with a much lower cooling rate than water, but for those workpieces with high hardenability, small size, complex shape and large deformation tendency, the cooling rate of oil is too high, but for workpieces with small size but poor Hardenability, in refrigerationem rate of oleum est insufficiens. Ut solvere supra contradictionibus et plenum usum olei extinguere ad redigendum quod extinguetur deformatio workpieces, qui adoptavit modos ad adjusting oleum temperatus et augendae extinxit temperatus ad expand et oleum.
-Changing temperatus de extinguendo oleum: using the same oil temperature for quenching to reduce quenching deformation still has the following problems, that is, when the oil temperature is low, the quenching deformation is still large, and when the oil temperature is high, it is difficult to ensure that the workpiece post extinguendas duritiam. Sub combined effectus ex figura et materia quaedam workpieces, augendae temperatus ex extinguendo oleum potest etiam auget eius deformatio. Ideo non est ipsum necessarium determinare oleum temperatus de extinguendo oleum post transeuntes in test secundum actualem condicionibus workpiece materia, crucem-sectional magnitudine et figura.
Cum usura calidum oleum ad extinxit, ut ne ignis causatur a magno oleum temperatus per extinxit et refrigerationem, necessaria ignis pugnae apparatu instructi prope oleum tristique. In addition, qualis index ex extinguendo oleum debet esse probata regulariter, et novum oleum debet replevi vel reponi in tempore.
-Increase in extinguitur temperatus: Hoc modo est idoneam ad parva crucem-section carbon ferro workpieces et leviter maius allymes ferro workpieces quod non occurrit duritia requisita post calefacit et calor conservationem ad normalis extinguat temperaturis et oleum extinguere. Per appropriately augendae extinxit temperatus et oleum extinxit, effectum de induratione et reducendo deformatio potest effectum. Cum per hoc modum extinguere, curare debet capta ne difficultates ut frumenti coarsoening, reductionem mechanica proprietatibus et servitium vitae workpiece debitum ad aucta extinguetur temperatus.
-Classification et austemperingCum extinguendo duritia potest obviam consilio requisitis, per gradus et austum calidum balneum medium debet esse plene usus ad consequi ad reducendo extinguetur deformatio. Hoc modum etiam efficax humilis-hardenenability, parva-sectione ipsum fabrica ferro et instrumentum ferro, praesertim chromium, quibus mori ferro et summus celeritate ferro workpieces cum princeps hardenenability. In genere calidum balneum medium et refrigerationem modum austempering sunt basic extinguat modi huiusmodi ferro. Similiter etiam efficax ad illos carbonis steels et humilis-alley structurae Steels, qui non requirere excelsum extinguantur duritia.
Cum extinguendo cum calidum balneum, sequenti quaestiones solvit operam;
Primo, cum oleum balneum adhibetur ad gradatim et isothermal extinxit, et oleum temperatus debet esse stricte imperio ne occulto ignem.
Secundo cum extinguendo nitrate sal grades, nitrate sal cisternina instructi necessaria instrumenta et aqua refrigerationem cogitationes. Nam alia cautiones, placere ad pertinet notitia et non repetere eos.
Tertio, in isothermal temperatus debet esse stricte imperium in isothermal extinguitur. High vel humilis temperatus non conducit ad redigere extinguetur deformatio. Insuper per austumpering, pendens modum in workpiece debet electus ne deformatio per pondus workpiece.
Quarto, cum per isothermal vel gradus extinguere ad corrigere figura de workpiece dum est calidum, in tooling et fixtures sit plene instructa et actum sit celeri per operationem. Ne adversa effectus in extinxit qualis est workpiece.
Refrigerandum operatio: SCITUS operatio in refrigerationem processus habet a significant ictum in extinguere deformatio, praesertim cum aqua vel oleum extinguat media sunt.
-Correct Direction of Quenching Medium Entry: Typice, symmetrically libratum vel elongatae virga, sicut workpieces sit directe extinguetur in medium. Asymmetric partes potest extinguere ad angulum. Recte directionem tendit ad curare uniformis refrigerationem per omnes partes, cum tardius refrigerationem locis intrantes medium primum, sequitur per citius refrigerationem sectiones. Consideratio de workpiece scriptor figura et ad influentiam in refrigerationem celeritate est vitalis in usu.
-Movement of workpieces in extensionem medium: Tardus refrigerationem partes debet faciem extinguantur medium. Symmetrically informibus workpieces sequatur a libratum et uniformis semita in medio, maintaining parva amplitudine et velox motus. Nam tenues et elongatae workpieces, stabilitatem in extinguendo est crucial. Vitare inclinata et considerans usura fibulis pro filum binding pro meliorem imperium.
-Speed de Quenching: Workpieces sit extinguetur cursim. Praecipue tenuis, virga, sicut workpieces, tardior extinxerit celeritates ad augeri flexionem deformatio et differentias deformatio inter sectiones extinguetur diversis temporibus.
-Controlled Refrigerant: Nam workpieces cum significant differentias in crucem-section Size, protegat citius, refrigerationem sectiones cum materiae sicut asbesto funem vel metallum rudentis ad redigendum eorum refrigerationem rate et consequi uniformis refrigerationem.
-Cooling in tempore aqua: Nam workpieces maxime experiencing deformatio debitum ad structural accentus, brevi eorum refrigerationem tempore in aquis. Nam workpieces praesertim subeunda deformatio debitum ad scelerisque accentus, extendens refrigerationem tempore in aquam ad redigendum extinguetur deformatio.
Edited by May Jiang a Mat Aluminium